Li4Mo5O17 crystal as possible scintillating material: Growth and luminescence properties

Li4Mo5O17 crystal as possible scintillating material: Growth and luminescence properties Научная публикация

Журнал

Journal of Crystal Growth
ISSN: 1873-5002 , E-ISSN: 0022-0248

Вых. Данные

Год: 2024, Том: 627, Номер: 127520, Номер статьи : 127520, Страниц : 8 DOI: 10.1016/j.jcrysgro.2023.127520

Ключевые слова

Czochralski techniqueLow temperature gradientsCrystal growth from meltLi4Mo5O17Photoluminescence

Авторы

Grigorieva V.D. ^1,2 , Kuznetsov A.B. ³ , Ryadun A.A. ^1,2 , Kremlev A.D. ^1,2 , Yudin V.N. ^1,2 , Шлегель Владимир Николаевич ¹

Организации

1	Nikolaev Institute of Inorganic Chemistry SB RAS, Novosibirsk 630090, Russia
2	Novosibirsk State University, Novosibirsk 630090, Russia
3	Sobolev Institute of Geology and Mineralogy SB RAS, Novosibirsk 630090, Russia

Transparent Li4Mo5O17 crystals with dimensions 60 × 30 × 20 mm were grown by low-thermal-gradient Czochralski technique. Optimal growth parameters were determined. According to SCXRD, Li4Mo5O17 compound crystallizes in the triclinic space group of P and the unit cell parameters at 150 K are a = 6.7596(2) Å, b = 9.4546(3) Å, c = 10.7909(3) Å, α = 73.1610(10)°, β = 88.8810(10)°, γ = 69.7460(10)°, V = 616.75(3) Å3. Uniformity of obtained crystals was confirmed by XRD analysis. Li4Mo5O17 crystal structure and cell parameters were studied by SCXRD. Li4Mo5O17 melting point at 546 °C was determined by DSC curve in 300–1000 K range. Luminescence was registered with peak maximum 670 nm at 370 nm excitation and 645 nm at 300 nm excitation.

Grigorieva V.D. , Kuznetsov A.B. , Ryadun A.A. , Kremlev A.D. , Yudin V.N. , Shlegelʹ V.N.
Li4Mo5O17 crystal as possible scintillating material: Growth and luminescence properties
Journal of Crystal Growth. 2024. V.627. N127520. 127520 :1-8. DOI: 10.1016/j.jcrysgro.2023.127520 WOS Scopus РИНЦ OpenAlex

Поступила в редакцию:	18 окт. 2023 г.
Принята к публикации:	4 дек. 2023 г.
Опубликована online:	7 дек. 2023 г.
Опубликована в печати:	1 февр. 2024 г.

Web of science:	WOS:001140253300001
Scopus:	2-s2.0-85182212966
РИНЦ:	65690057
OpenAlex:	W4389463284

БД	Цитирований
OpenAlex	4
Web of science	2